An Investigation of Relationship Between Corrosion Behaviour- Fe Tolerance Limit in Az91 Mg Alloys

Abstract

In this study, relationshipbetween Corrosion Behaviour-Tolerance Limit of Fe content (0.025, 0.05, 0.1 wt.%) in AZ91 Mg alloys, cast under similar chemical composition and cooling rate,were investigated. The microstructures of Mg alloys were analysed by ScanningElectron Microscopy (SEM) and X Ray Diffractometry (XRD). The corrosionbehaviours were evaluated by immersion tests and electrochemical polarizationmeasurements in 3.5 wt. % NaCl solution. Microstructure analysis revealed thatthe increase of Fe content increased the “partially divorced” or “lamellaeutectic” type ? phase morphologies in the microstructure. Results indicatedthat the limit content value of Fe in AZ91 alloys was ~0.05 wt. % above which thecorrosion loss had increased abruptly.Bu çalışmada, aynı şartlarda üretilmiş (benzer katılaşma hızı ve benzerkimyasal bileşimde) farklı Fe içeriğine (% ağ. 0.025, 0.05, 0.1) sahip AZ91 Mg alaşımlarınınkorozyon davranışları-Fe tolerans limit değeri arasındaki ilişkideğerlendirilmiştir. Numunelerin mikro yapı analizleriTaramalı Elektron Mikroskobu (SEM) ve X Işını Difraktometre (XRD) kullanılarakyapılmıştır. Korozyon davranışları %3,5 NaCl çözeltisinde, ağırlık kaybıve potansiyodinamik polarizasyon test yöntemleri kullanılarak araştırılmıştır. Mikroyapıanalizlerinde, Fe içeriğinin artması ile yapıdaki “kısmen ayrışmış” veya “lamellerötektik” tipi ? fazı morfolojilerinde artış eğiliminin daha fazla olduğugözlenmiştir. Sonuçlar, AZ91 alaşımı Fe tolerans limit değerinin ~%0.05 olduğunu bu değerden sonra korozyon kaybının eksponansiyel olarakarttığını göstermiştir.