Title: | Effect of thermal degradation on the properties and wear behavior of Cr-V-C composite coatings grown on ductile iron | Authors: | Günen, Ali Kanca, Erdoğan Karakaş, Mustafa Serdar Gök, Mustafa Sabri Kalkandelen, Müge Kurt, Bülent Karahan, İsmail Hakkı |
Keywords: | Ductile Iron Trd Treatment Wear Thermal Degradation Nodular Cast-Iron Dry Sliding Wear Of-The-Art Fatigue Resistance Thermomechanical Fatigue Graphite Nodules Temperature Surface Layer |
Publisher: | ELSEVIER SCIENCE SA | Abstract: | The thermal fatigue behavior of chromium vanadium carbide (Cr - V - C) coatings and the wear of the coatings after thermal fatigue cycling was studied. The Cr - V - C coatings were grown on the surface of a ductile iron using thermo-reactive diffusion (TRD) and subjected to thermal fatigue in the temperature range of 25 to 750 degrees C for up to 500 cycles. Characterizations were made using scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, microhardness measurements and wear tests. The Cr - V - C coated samples displayed superior thermal fatigue and wear resistance compared to the untreated ductile iron, mainly due to the dissolution of graphite nodules in the vicinity of the surface during TRD. The dissolution of graphite reduced the possibility of failure initiating from graphite nodules and graphite-matrix interfaces. Increasing the number of cycles resulted in increased flaking and decreased wear resistance in both the Cr - V - C coatings as well as the untreated ductile iron. Although much of the Cr V C coating was lost (due to flaking) after thermal cycling, the absence of graphite near the surface still provided improved resistance to wear in the TRD-treated samples. The results of this study indicate that TRD coatings hold great promise for use in the industrial applications. | URI: | https://doi.org/10.1016/j.surfcoat.2021.127305 https://hdl.handle.net/20.500.13091/657 |
ISSN: | 0257-8972 1879-3347 |
Appears in Collections: | Mühendislik ve Doğa Bilimleri Fakültesi Koleksiyonu Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collections WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collections |
Files in This Item:
File | Size | Format | |
---|---|---|---|
1-s2.0-S0257897221004795-main.pdf Until 2030-01-01 | 19.95 MB | Adobe PDF | View/Open Request a copy |
CORE Recommender
SCOPUSTM
Citations
2
checked on Apr 20, 2024
WEB OF SCIENCETM
Citations
10
checked on Apr 20, 2024
Page view(s)
80
checked on Apr 22, 2024
Download(s)
6
checked on Apr 22, 2024
Google ScholarTM
Check
Altmetric
Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.