Title: Sınıfsız Afsin-Elbistan Uçucu Külü ve Atık Cam Tozundan Yapılan Harçların Özellikleri
Other Titles: PROPERTIES OF MORTARS PRODUCED WITH CLASSLESS AFSIN-ELBISTAN FLY ASH AND WASTE GROUND GLASS
Authors: Binici, Hanifi
Eken, Mustafa
Uslu, Kenan
Keywords: ASR
Uçucu kül
Dayanım
Cam tozu
ASR
Fly ash
Strength
Ground Glass
Publisher: Konya Technical University
Abstract: The aim of the present study to investigate classless Afsin-Elbistan fly ash. For this purpose, classless Afsin-Elbistan fly ash and waste granulated glass have been mixed at certain rates. After several experiments, obtained mixture according to standard were determined. The mortar samples produced by these mixtures with different percentages replaced of cement. Setting time, volume expansion, flexural and compressive strengths of samples were determined at 3-7-28 days. Moreover, alkali-silica reaction (ASR) of samples was tested according to using mortar bar experiments. The results of this study, Afsin-Elbistan fly ash can be used as C and F class ash in accordance. The best results of flexural and compressive strengths of samples were obtained by fifteen percent ground glass added. Expansion ratio of the samples was within the limits given standard. From the results that has been founded many properties of the mortars are better than that of the References samples. This study has shown that the addition waste ground glass to classless ash can be used as a C or F class ash.
The aims of the present study to investigate classless Afsin-Elbistan fly. For this purpose, classless Afsin-Elbistan fly ash and waste granulated glass have been mixed at certain rates. After several experiments, obtained mixture according to standard were determined. The mortar samples produced by these mixtures with different percentages replaced of cement. Setting time, volume expansion, flexural and compressive strengths of samples were determined at 3-7-28 days. Moreover, alkali-silica reaction (ASR) of samples was tested according to using mortar bar experiments. The results of this study, Afsin- Elbistan fly ash can be used as C and F class ash in accordance. The bending and compressive strengths of the samples that added ten percent glass powder to the fly ash were found to be the highest. The expansion rates of the samples were found in accordance with the standard. The results obtained from experimental studies have shown that many properties of mortars produced with class ash are better than the Reference sample. The results of this study showed that by adding different amounts of glass powder to the Afsin- Elbistan fly ash, it could be used in cement production as the ash was classified into class.
Description: DergiPark: 825996
konjes
URI: https://doi.org/10.36306/konjes.825996
https://dergipark.org.tr/tr/pub/konjes/issue/62624/825996
https://dergipark.org.tr/tr/download/article-file/1397348
https://hdl.handle.net/20.500.13091/2188
ISSN: 2667-8055
Appears in Collections:Konya Mühendislik Bilimleri Dergisi

Files in This Item:
File SizeFormat 
10.36306-konjes.825996-1397348.pdf682.6 kBAdobe PDFView/Open
Show full item record



CORE Recommender

Page view(s)

350
checked on Mar 25, 2024

Download(s)

122
checked on Mar 25, 2024

Google ScholarTM

Check




Altmetric


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.