Yurtdaş, SemihKaraman, MustafaTozlu, Cem2022-02-262022-02-2620212667-8055https://doi.org/10.36306/konjes.972477https://dergipark.org.tr/tr/pub/konjes/issue/67514/972477https://dergipark.org.tr/tr/download/article-file/1884686https://hdl.handle.net/20.500.13091/2007DergiPark: 972477konjesIn this study, the effect of the molarity of ZnO synthesized by the sol-gel method on the efficiency of P3HT (Poly (3-hexyl thiophene)):PCBM ((6,6) Phenyl-C61-Butyric acid methyl ester) active layer solar cell was investigated. It was studied at 0.1, 0.3 and 0.5 M values. The efficiency values of the devices were determined with the Keithley 2400 source meter under 100 mw/cm2 solar radiation. In addition, characterization processes were carried out with XRD, UV-Vis and FESEM techniques. After the studies, it was found that 0.1 M synthesis concentration was the most suitable condition and it was determined that 3.09% efficiency could be reached with the device produced under these conditions.Bu çalışmada, sol-jel yöntemi ile sentezlenmiş ZnO molaritesinin P3HT (Poli (3-hekzil tiyofen)):PCBM ((6,6) Fenil-C61-Bütirik asit metil ester) aktif tabakalı güneş hücresinde verime olan etkisi incelenmiş ve 0,1, 0,3 ve 0,5 M değerlerinde çalışılmıştır. Aygıtların verim değerleri, 100 mw/cm2 güneş ışıması altında Keithley 2400 kaynak ölçer cihazı yardımı ile belirlenmiştir. Ayrıca XRD, UV-Vis ve FESEM teknikleri ile karakterizasyon işlemleri gerçekleştirilmiştir. Yapılan çalışmalar sonrasında 0,1 M sentez konsantrasyonunun, en uygun koşul olduğu bulunmuş ve bu şartlarda üretilen aygıt ile %3,09 verime ulaşılabildiği tespit edilmiştir.eninfo:eu-repo/semantics/openAccessZnOElectron transport layerPolimer solar cellsZnOElektron taşıyıcı tabakaPolimer güneş hücreleriArticle10.36306/konjes.972477