Title: Keten elyaf takviyesi ile hibritleştirmenin CTP kompozitlerin darbe dayanımına etkilerinin deneysel olarak araştırılması
Other Titles: Experimental investigation of the effects on impact strength of hybridization of GFR polymer composites with flax fiber reinforcement
Authors: Dağhan, Behcet
Kozan, Uğur
Keywords: Makine Mühendisliği
Mechanical Engineering
Issue Date: 2022
Publisher: Konya Teknik Üniversitesi
Abstract: Yapılan bu tez çalışmasında, E-cam elyaf takviyeli epoksi kompozit (CTPK) malzeme daha düşük maliyetli ve çevre dostu olabilmesi adına, keten elyaf ile hibritleştirilmiş ve düşük hızlı darbe testlerine tabi tutulmuştur. Bu kapsamda cam/keten elyaf takviyeli hibrit kompozitler (CKTPK) farklı yığılma sıraları ve farklı açılar ile dizilerek, vakum infüzyon yöntemi ile üretilmiştir. Üretilen her bir numune 150X100 mm boyutlarında kesilmiş ve test cihazına dört tarafından ankastre olacak şekilde yerleştirilmiştir. Daha sonra numunelere düşey ağırlık düşürme darbe test cihazında 2 m/s ve 3 m/s hızlarında 5,6 kg vurucu kütlesi ile darbe uygulanmıştır. Yapılan testler sonucunda malzemelerin dinamik cevabı, oluşan hasar modları ve mekanik özellikleri incelenmiştir.
In this thesis study, to be low cost and environment friend, E-glass fiber reinforced epoxy composite was hybridized with flax fibers and practiced to low velocity impact tests. Here, glass/flax reinforced hybrid composites were produced with different stacking sequences and different angles by using vacuum infusion method. Each specimen, having been produced, was cut out by dimensions of 150x100 mm and attached to tester as fixed from four sides. Then impact was applied with 5,6 kg mass of impactor and velocities of 2 m/s and 3 m/s. After tests was conducted, dynamic response, damage modes, and mechanical properties of the materials were investigated.
URI: https://tez.yok.gov.tr/UlusalTezMerkezi/TezGoster?key=CG8WvdvvxJP04Unr7Yecf3XTj7EOXez3dVuMfmrl_zGIuPksYszRL9rHv054MaWV
https://hdl.handle.net/20.500.13091/2313
Appears in Collections:Tez Koleksiyonu

Files in This Item:
File SizeFormat 
722068.pdf6.19 MBAdobe PDFView/Open
Show full item record

CORE Recommender

Page view(s)

162
checked on Feb 6, 2023

Download(s)

128
checked on Feb 6, 2023

Google ScholarTM

Check


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.